ANALYSIS OF MECHANICAL PROPERTIES OF PARTICLE BOARD BASED DURIAN SKIN AND SUGAR CANE BAGASSE WITH FORMALDEHIDA UREA ADHESIVE
Abstract
The particle board was made based on mixing durian skin and sugar cane bagasse with urea formaldehyde adhesive. The variations the composition of mixing durian skin, sugar cane bagasse with urea formaldehyde adhesive used among other: 35%:35%:30%, 30%:30%:40%, and 25%:25%:50% and printing time and pressing for 24 hours. The parameters of the testing include: Modulus of Rupture (MOR) dan Modulus of Elasticity (MOE). Analysis of the mechanical properties of the particle board produced at the composition of 35%:35%:30% which has a value MOR = 446,17 kgf/cm2 and MOE = 160,9 kgf/cm2, at the composition of 30%:30%:40%, has a value MOR = 1369,57 kgf/cm2 dan MOE = 3903,3 kgf/cm2, at the composition of 25%:25%:50%, has a value MOR = 1463,07 kgf/cm2, dan MOE = 3342,1 kgf/cm2 which matches SNI 03-2105-2006 criteria type 8 is not required.
Full Text:
PDF (Indonesian)References
Adlina, Elfrida. 2016. Pengaruh Kadar Perekat Urea Formaldehida Terhadap Kualitas Papan Partikel Kulit Buah Markisa (Passiflora Edulis). Skripsi. Program Studi Kehutanan Fakultas Kehutanan. Universitas Sumatera Utara.
Ana, Dwi A, Dkk. 2015. Potensi Limbah Kulit Durian Sebagai Bahan Baku Pembuatan Energi Alternatif. Jurnal Seminar Nasional Teknologi.
Anggita. 2018. Pembuatan Papan Partikel Berbahan Campuran Kulit Pinang (Areca Catechu L) dengan Ampas Tebu (Saccarum Oficianarum). Skipsi. Program Studi Keteknikan Fakultas Pertanian. Universitas Sumatera Utara.
Diba, Farah, dkk. 2014. Sifat Fisik dan Mekanik Papan Partikel dari Kulit Durian (Durio Sp) dengan Konsentrasi Urea Formaldehida yang Berbeda. Jurnal Hutan Lestari. Vol 2. No 3.
Haloho, Krismes Santo. 2018. Pengaruh Kadar Perekat Urea Formaldehida terhadap Sifat Fisika dan Mekanika Papan Partikel Limbah Gergaji Kayu Alau (Dacridium spp). Skripsi. Fakultas Pertanian. Universitas Palangka Raya.
Maloney, T.M. (1993). Modern Particle board and dry process Fiberboard. Manufacturing. USA: MilerFreeman Publication.
Nuryaman, A., Iwan, R., dan Pamona, S.N. (2009). Sifat Fisik Mekanik Papan Partikel dari Limbah Pemanenan Kayu. Jurnal Ilmu dan Teknologi Hasil Hutan.
Purba, Astari. 2018. Sifat Fisis dan Mekanis Papan Partikel dari Beberapa Bahan Berlignoselulosa dengan Perekat Isosianat.Skripsi. Program Studi Teknologi Hasil Hutan Fakultas Kehutanan. Universitas Sumatera Utara.
Riska, dkk.2015. Pembuatan Papan Partikel Berbahan Dasar Kulit Durian. Jurnal Rekayasa Pangan dan Pertanian.4(4).
Simatupang, Friska. 2013. Pengaruh Ukuran Partikel dan Kadar Perekat Terhadap Sifat Fisis dan Mekanis Papan Partikel dari Limbah Batang Kelapa Sawit dengan Perekat Urea Formaldehida. Skripsi. Program Studi Kehutanan Fakultas Pertanian. Universitas Sumatera Utara.
Supriadi, Achmad. 2013. Pengaruh Kadar Perekat Terhadap Sifat Papan Partikel Ampas Tebu (The Effect of Adhesive Content on Properties Bagasse of Particleboard). Jurnal Penelitian Hasil Hutan. 31(1):19-26.
Suroto. 2010. Pengaruh Ukuran dan Konsentrasi Perekat Terhadap Sifat Fisik dan Mekanik Papan Partikel Limbah Rotan. Jurnal Riset Industri Hasil Hutan. 2(2) : 18-30.
Yani, Ahmad, dkk. 2018. Sifat Papan Partikel dari Campuran Kulit Kayu Rhizophora Apiculata BI DAN Acacia crassicarpa A. Cunn. Ex. Benth Berdasarkan Konsentrasi Perekat Urea Formaldehida. Jurnal Hutan Lestari. 6(3):473-485.
Yanto, Feri. 2015. Pengaruh Variasi Prosentasi Berat Urea Formaldehida Terhadap Sifat Mekanik Papan Partikel dari Tongkol Jagung dan Serat Kelapa. Skripsi. Program Studi Teknik Mesin Fakultas Teknik. Universitas Muhammadiyah Pontianak.
Yetri, Yuli. 2018. Pengaruh Komposisi Kulit Buah Kakao, Ampas Tebu, dan Perekat terhadap Sifat Fisis dan Mekanis Papan Partikel dari Campuran Limbah Kulit Buah Kakao dan Ampas Tebu. Jurnal Fisika Unand. 7(1).
DOI: http://dx.doi.org/10.30821/fisitek.v4i1.7918
Refbacks
- There are currently no refbacks.
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.
Prodi Fisika - Universitas Islam Negeri Sumatera Utara
Website : https://uinsu.ac.id/
FISITEK is licensed under a Creative Commons Attribution 4.0 International License